Sulfiding and reoxidation of chromium catalyst

ABSTRACT

High melt flow olefin polymers suitable for such applications as injection molding, and the like requiring a narrow molecular weight distribution are produced using a catalyst made by treating a chromium catalyst on a silica-containing base with a sulfur-containing material, and thereafter reoxidizing.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of copending application Ser. No. 857,556, filed Dec. 5,1977, now U.S. Pat. No. 4,177,162.

BACKGROUND OF THE INVENTION

This invention relates to the activation of chromium-containing olefin polymerization catalysts.

Supported chromium oxide catalysts can be used to prepare olefin polymers in a hydrocarbon solution to give a product having excellent characteristics from many standpoints. Supported chromium oxide catalysts can also be used to prepare olefin polymers in a slurry system wherein the polymer is produced in the form of small particles of solid material suspended in a diluent. This process, frequently referred to as a particle-form process, has the advantage of being less complex. However, certain control operations which are easily carried out in the solution process are considerably more difficult than the particle-form process. For instance, in the solution process, control of the molecular weight can be effected by changing the temperature with lower molecular weight (higher melt flow) being obtained at the higher temperature. However, in the slurry process, this technique is inherently limited since any effort to increase the melt flow to any appreciable extent by increasing temperature would cause the polymer to go into solution and thus destroy this slurry or particle-form process.

SUMMARY OF THE INVENTION

It is an object of this invention to provide a catalyst capable of giving high melt flow polymer; it is a further object of this invention to provide a catalyst suitable for use in slurry polymerization systems; it is a further object of this invention to provide an improved method of activating a chromium-containing catalyst; it is yet a further object of this invention to provide a catalyst capable of giving high activity in addition to high melt flow and narrow molecular weight distribution, and it is still yet a further object of this invention to provide a catalyst capable of giving polymer suitable for injection molding and other applications requiring high melt flow and narrow molecular weight distribution.

In accordance with this invention, a chromium catalyst on a silica-containingbase is contained with a sulfur-containing ambient and thereafter reoxidized.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The base can be any silica-containing material as broadly disclosed in Hogan et al, U.S. Pat. No. 2,825,721 (Mar. 4, 1958), the disclosure of which is hereby incorporated by reference. The base can contain, if desired, from 0.1 to 20 weight percent of materials other than silica, such as alumina as is known in the art. The chromium-containing silica base catalyst is preferably a cogel, that is, a catalyst produced by coprecipitating silica and a titanium-containing compound. Production of such cogels is described in Dietz, U.S. Pat. No. 3,867,494 (June 3, 1975), the disclosure of which is hereby incorporated by reference. Cogels can be formed, for instance, by adding a titanium compound to a mineral acid, introducing an alkali metal silica into the acid containing said titanium compound to form a hydrogel, aging the hydrogel for greater than one hour, washing the thus aged hydrogel to produce a substantially alkali metal free hydrogel, forming a mixture comprising the thus washed hydrogel and a normally liquid oxygen-containing water soluble organic compound, and separating said organic compound and water from said mixture to form a xerogel.

The catalyst contains chromium in an amount generally within the range of 0.001 to 10, preferably, 0.1 to 5, more preferably about 0.5 to 1 weight percent based on the weight of the silica-containing base. The chromium compound can be incorporated as known in the art. For instance, a hydrocarbon solution of a material such as tertiary butyl chromate can be used to impregnate the xerogel or an aqueous solution of a chromium compound such as chromium trioxide or chromium acetate can be added to the hydrogel before drying, or chromium can be coprecipitated along with the silica or the silica and titanium. Anhydrous hydrocarbon solutions of π-bonded organochromium compounds such as diarene chromium compounds or biscyclopentadienyl chromium II can be used. In U.S. Pat. No. 3,976,632 (Dec. 4, 1974); U.S. Pat. No. 3,349,067 (Oct. 24, 1967) and U.S. 3,709,853 (Jan. 9, 1973), the disclosures of which are hereby incorporated by reference, are disclosures of suitable chromium compounds.

As will be described in more detail hereinbelow, the chromium at the time it is contacted with the sulfur is at least partially, preferably predominantly in the hexavalent state. This can be achieved either by an air oxidation as will be described hereinbelow in greater detail or by incorporating the chromium initially simply by introducing the chromium in the form of chromium oxide. In the case of embodiments wherein the preliminary oxygen treatment is given prior to the sulfiding, the chromium in a lower valence state, for instance, in the +3 state is oxidized to the +6 state and water is driven off. Even in instances where the chromium is already in the form of CrO₃, it is frequently preferred to heat the material up to the sulfiding temperature in the presence of air. This gives a threefold benefit in that it dries the material to remove water, conserves more expensive nitrogen and results in a better final product since there is some disadvantage to allowing the material at this stage to come in contact with nitrogen at a high temperature since it tends to self-reduce, particularly in the presence of moisture.

One preferred sulfur-containing material is carbon disulfide. Other suitable materials include thiols or polythiols and sulfides or polysulfides which contain hydrocarbyl radicals containing from 1 to 20 or more carbon atoms. Other exemplary compounds include carbon monosulfide, carbon subsulfide, methanethiol, 2-methyl-1-propanethiol, eicosanethiol, benzenethiol, parabenzenedithiol, thiophene-2-thiol, 1,2,3-propanetrithiol, dimethylsulfide, diethylsulfide, diphenylsulfide, benzylphenylsulfide, dimethylsulfide, di-4-tolyldisulfide, 2'-dinaphthyldisulfide, diethyltrisulfide, thiophene, and the like. A sufficient amount of the sulfur compound is employed to react with at least a portion of the chromium present in the supported catalyst to form a chromium sulfide. The amount used can vary over a rather wide range. Generally, a weight ratio of supported catalyst organic sulfur compound ranging from about 100:1 to about 0.1:1, more preferably from about 20:1 to about 0.2:1 have been found suitable for this purpose. If a higher molecular weight sulfur-containing nonoxidizing agent is utilized, it can simply be used to impregnate the catalyst prior to heating instead of being added to the ambient as is done with more volatile sulfur-containing agents.

It is then found particularly beneficial to include an oxygenated compound, such as an alcohol, carboxylic acid or even water vapor with the thiols and sulfides since reproducibility of results is promoted. For instance, a mixture of acetic acid and carbon disulfide can be used. Alternatively, a single material, such as carbonyl sulfide can be utilized which contains both oxygen and sulfur. Generally, a mole ratio of organic sulfur compound to oxygenated compound ranging from about 0.1:1 to 10:1 is employed since consistently high melt index values for polymer produced over such catalysts have been obtained.

Suitable alcohols include saturated and unsaturated aliphatic and aromatic alcohols with boiling points of about 300° C. or less as a matter of convenience. Particularly preferred alcohols from an economic standpoint and ready availability are methanol and isopropanol. These can decompose into H₂ and CO.

Suitable carboxylic acids include saturated and unsaturated compounds which are normally liquid as a matter of convenience. A fatty acid, particularly acetic acid, is presently preferred because of ready availability and low cost. These can decompose into various mixtures of C, CO, CO₂ and H₂.

The sulfiding step can be carried out by fluidizing the dry catalyst (chromium on a silica-containing base) with the nitrogen. This removes air or oxygen if air or oxygen has been used as the ambient for heating to sulfiding temperature. If nitrogen has been used initially, then, of course, the same nitrogen fluidization can continue. It is preferred that the contact of the oxidized catalyst with nitrogen at this elevated temperature before sulfiding be very short, preferably less than 30 minutes, more preferably less than 5 minutes, most preferably about 1 minute or less, i.e. the minimum time required to remove oxygen to prevent self-reduction of the Cr in the catalyst. Also, if an oxygen-containing gas such as air is used in the initial heating, it is essential to remove it since the contact at this temperature between oxygen and sulfur-containing materials such as CS₂ might result in uncontrolled oxidation.

The sulfur-containing material is then introduced most conveniently simply by introducing a stream of the sulfur-containing material into the nitrogen stream. After the sulfiding step is complete, the catalyst is adjusted to the reoxidation temperature which may be the same as the sulfiding temperature but which is preferably at least 50° C., more preferably 100°-300° C., lower than the sulfiding temperature.

The reoxidation can take place in any oxidizing ambient containing oxygen, the preferred ambient, of course, being air. Air nitrogen mixtures containing 10-100% air and 0-90% nitrogen can be utilized (gas percentages are all in volume percent). In addition, oxidizing ambients such as NO₂, N₂ O, and oxygen-containing halogen materials such as I₂ O₅ or Cl₂ O can be utilized.

The temperature for the treatment with air prior to sulfiding, if used at all, is generally from room temperature up to the sulfiding temperature, although it is contact with the air at a temperature of 250°-1000° C., preferably 700°-925° C., that is most important. The time can simply be whatever time is required to heat the material to sulfiding temperature and generally will be greater than 5 minutes, preferably 5 minutes to 15 hours, more preferably 20 minutes to 10 hours, most preferably 40 minutes to 3 hours. The heating may be continuous or stopped at any point within the above recited temperature ranges. The temperature for the sulfiding step is within the broad range of 370°-1000° C., preferably 600°-900° C., more preferably 700°-900° C. The times can be relatively short, generally greater than 1 minute, preferably 5 minutes to 10 hours, more preferably 10 minutes to 3 hours.

The subsequent reoxidation temperatures, as noted hereinbefore, are preferably lower than those used for the sulfiding and generally will be in the range of 350°-900° C., or 400°-900° C., preferably 450°-700° C.

The time required for the reoxidation is at least 5 minutes, preferably 1/2 to 10 hours, more preferably 1 to 4 hours.

With regard to the sulfiding temperature being relatively high, it is noted that the chromium is converted to a sulfide at temperatures below 260° C., however, for some unexplained reason, sulfiding temperatures must be substantially higher than this to be effective.

The final catalyst can contain 0-0.5, preferably less than 0.4, more preferably less than 0.3 weight percent S based on the weight of the support.

If hydrocarbons are used at any stage during the activation process, it is generally necessary to follow the hydrocarbon treatment with an ambient containing a relatively low amount of oxygen so as to carefully burn off the carbon.

If desired, the catalyst of this invention can be activated in a continuous activator. For instance, catalyst can be introduced at the top of a compartmentalized vertical activator with the first gas to be used in treating the catalyst being introduced at the bottom of the first (upper) compartment and taken off near the top thereof. The second gas is introduced near the bottom of the second (lower) compartment and taken off near the top thereof and if three or more gases are used, the process can continue in a like manner. In each compartment, the catalyst would be fluidized with the treating medium. Alternatively, two or more compartments could be utilized with the gaseous treating medium, if desired, to increase residence time. An external furnace can heat each compartment to the desired temperature. While a continuous activator was not used to produce the catalysts of the examples set out hereinbelow, the use of a continuous activator was simulated by introducing the catalyst initially into an activator which was at an elevated temperature. It was found that in the embodiments wherein the initial heating is done in a nonoxidizing atmosphere, problems sometimes associated with introducing catalysts in the presence of air into an already heated activator were not encountered.

The catalysts of this invention can be used to polymerize at least one mono-1-olefin containing 2 to 8 carbon atoms per molecule. The invention is of particular applicability in producing ethylene homopolymers and copolymers from mixtures of ethylene and 1 or more comonomers selected from 1-olefin and/or dienes containing 3 to 8 carbon atoms per molecule. Exemplary comonomers include aliphatic 1-olefins, such as propylene, 1-butene, 1-hexene, and the like and conjugated or nonconjugated diolefins, such as 1,3-butadiene, isoprene, piperylene, 2,3-dimethyl-1,3-butadiene, 1,4-pentadiene, 1,7-hexadiene, and the like and mixtures thereof. Ethylene copolymers preferably constitute about 90, preferably 95 to 99 mole percent polymerized ethylene units. Ethylene, propylene, 1-butene and 1-hexene are especially preferred.

The polymers can be prepared from the activated catalysts of this invention by solution polymerization, slurry polymerization, and gas phase polymerization techniques using conventional equipment and contacting processes. However, the catalysts of this invention are particularly suitable in slurry polymerizations for the production of high melt index (MI) polymers, i.e. polymers having MI values in the 8 to 60 range and above in the absence of molecular weight modifiers, such as hydrogen, and with a molecular weight distribution value sufficiently narrow to be of commercial interest for applications such as injection molding. The slurry process is carried out in an inert diluent such as a paraffin, aromatic or cycloparaffin hydrocarbon at a temperature at which the resulting polymer is insoluble. For predominantly ethylene polymers, the temperature is about 66°-110° C. For example, ethylene homopolymers exhibiting a melt index in the 8 to 60 range can be obtained at the polymerization temperatures used in the examples by contact with the catalyst of this invention, whereas otherwise identical catalysts conventionally activated yield 5 to 6 MI polymers or lower. The high MI polymers have HLMI/MI ratio values ranging from about 33 to 38 with M_(w) /M_(n) values of about 4 at the polymerization temperatures used in the examples. Such resins can be injection molded in conventional apparatus to form tough, low warpage articles. The MI goes up and the HLMI/MI ratio goes down at higher reactor temperatures. Thus, for any comparison between the invention runs and control runs to be meaningful, they must be carried out at the same polymerization temperature.

The catalysts of this invention can be used with conventional cocatalysts such as triethyl aluminum if desired. Also, hydrogen can be used to further increase the MI if desired.

EXAMPLE 1

Unless otherwise indicated, the raw catalyst employed in the activation procedures was a coprecipitated silica-titania gel (cogel) comprising about 2 weight percent titanium, calculated as the metal on a dry basis. Sufficient chromium acetate solution was used to impregnate the wet gel toimpart 0.82 weight percent chromium, calculated as the metal on a dry basisof the composite. Following impregnation, the wet composite was dried by means of extraction with liquid ethyl acetate. The resulting dried catalyst is designated as stock catalyst.

A 48 mm O.D. quartz tube was charged in each run with a 50 ml (10.9 g) portion of the stock catalyst. The charge was heated to 1600° F. (871° C.) using a heat-up rate of 3°-5° C. per minuteand in the presence of a dry air flow rate of about 42 liters per hour. Theflow rate corresponds to a superficial linear velocity at 1600° F. of 0.1 foot (0.3 cm) per second. The air was cut off and dry nitrogen at the same flow rate was substituted for it to flush air from the activator for 1 minute. Then 1 ml (1.26 g) of carbon disulfide was injected onto a glass wool plug located in the bottom of the activator through which nitrogen flowed up to the catalyst. Evaporation of the liquid was completewithin 2 to 3 minutes. The weight ratio of catalyst treated to carbon disulfide was about 8.6:1. The treated catalyst was held at 1600° F. in the nitrogen stream for an additional 2 hours after which the activator temperature was lowered to the reoxidation temperature while continuing the nitrogen stream. When the desired temperature was reached, dry air was substituted for the nitrogen and the catalyst was heated in the air stream for 2 hours. Finally, the activator was cooled down while maintaining the air flow and the recovered catalyst was stored for later use.

Portions of each activated catalyst was charged to a reactor containing 1.5lbs. (682 g) isobutane, ethylene was admitted until 550 psig (3.8 MPa) was reached and polymerization was started. Additional ethylene was admitted on demand during each run as needed. The melt index value given in each run is corrected to 5000 g polymer per g catalyst productivity level to provide a comparative basis for judging the results.

Details of the analyzed sulfur and chromium(VI) contents of each catalyst, reoxidation temperature employed, catalyst color obtained and melt index of polymer made using that catalyst are presented in Table I.

                                      TABLE I                                      __________________________________________________________________________     Ethylene Polymerization With Cogel Catalyst Sulfided With CS.sub.2                Reoxidation                                                                           Weight                                                               Run                                                                               Temperature                                                                           Percent                                                                             Percent                                                                             Catalyst                                                                             Polymer                                                                              Run Temp.                                      No.                                                                               °C.                                                                            Sulfur                                                                              Cr(VI)                                                                              Color Melt Index                                                                           °C.                                     __________________________________________________________________________     1  --     0.07 0    white none made                                                                            --                                             2  --     0.85 0    black none made                                                                            --                                             3  482    0.33 0.42 red brown                                                                            19    107                                            4  593    0.24 0.48 red brown                                                                            18    107                                            5  593    0.18 0.56 salmon                                                                               20    107                                            6  649.sup.(a)                                                                           <0.05                                                                               0.66 red orange                                                                           25    107                                            7  649.sup.(a)                                                                           <0.05                                                                               0.72 red orange                                                                           27    109                                            __________________________________________________________________________     Notes:                                                                          .sup.(a) Sulfiding was done at 649° C. rather than at 871°       C.                                                                       

Runs 1 and 2 of Table I are control runs. Run 1 shows that the cogel in theabsence of any chromium is unchanged in color by the activation treatment and the treated gel is not an active polymerization catalyst. Run 2 shows that the sulfiding treatment turns the cogel containing chromium black in color and that no chromium(VI) is present under such reducing conditions. It is believed that chromium sulfide, Cr₂ S₃ or CrS, is formed and the results show the composite in that state is not an active polymerization catalyst. Invention catalysts are shown in runs 3-7 after reoxidation of the sulfided composites. The results show that catalysts containing from less than about 0.05 to about 0.3 weight percent sulfur are active ethylene polymerization catalysts when the chromium(VI) contentranges from 0.4 to about 0.7 weight percent based on the weight of the dry cogel. The invention catalysts all exhibit a characteristic reddish hue after the activation treatment.

EXAMPLE 2

Portions of the stock catalyst described in Example 1 were individually activated in the presence of CS₂ at various temperatures and reoxidized in air at various temperatures using the activator and gas flowrates reported earlier. Portions of each catalyst was used to polymerize ethylene as before. Activation conditions employed and results obtained are given in Table II.

                                      TABLE II                                     __________________________________________________________________________     Relationship Of Catalyst Sulfiding Conditions On Polymer Melt Index                                       Polymerization                                                                             Polymer                                 Run                                                                               Activation                                                                           Sulfiding                                                                            Reoxidation                                                                          Catalyst                                                                             Run Temp.                                                                            Run Time                                                                             Adjusted                                                                            HLMI                                                                               Productivity                   No.                                                                               Process.sup.(1)                                                                      Temp., ° C.                                                                   Temp., °C.                                                                    Color °C.                                                                           (min.)                                                                               MI.sup.(3)                                                                          MI  g/g cat.                       __________________________________________________________________________     1  A     260   593   green 107   77    5.4  40  4810                           2  A     399   593   tan   107   38    7.1  41  4900                           3  A     538   593   tan   107   48    9.5  39  5120                           4  B     538   538   orange                                                                               102   80    0.08 76  5140                           5  B     649   649   orange                                                                               102   46    0.47 66  4270                           6  A     649   593   red orange                                                                           107   45    25   37  4980                           7  A     677   593   red orange                                                                           107   43    31   36  5110                           8  B     760   760   orange                                                                               102   32    0.89 69  4720                           9  B     871   871   orange                                                                               102   35    0.69  124.sup.(2)                                                                       4710                           10 A     871   593   red tan                                                                              102   59    18   44  5460                           11 C     --    --    orange                                                                               102   34    1.3  64  5080                           __________________________________________________________________________      .sup.(1) Activation Process                                                   A. Air to sulfiding temperature, switch to N.sub.2 (time too short and          temperature too low for any significant selfreduction) and inject 1 ml         CS.sub.2 into N.sub.2 stream, raise temperature to 871° C. and hol     at 871° C. while maintaining N.sub.2 flow, cool to 593° C. i     N.sub.2, switch to air and hold for 1 hour, then cool and recover.             B. Air to sulfiding temperature, switch to N.sub.2 and inject 1 ml CS.sub.     into N.sub.2 stream, hold 2 hours in N.sub.2 at that temperature, switch t     air and hold additional 2 hours at that temperature, then cool and recover     Results not as good because best results are obtained when the sulfiding        temperature is relatively high and the reoxidation temperature is lower.       In procedure A, although the listed sulfiding temperatures are sometimes       as low or lower, it was always raised to 871° C.                       C. Control air activation at 871° C. with no sulfiding.                  .sup.(2) Probably experimental error.                                          .sup.(3) Adjusted slightly to 5000 g/g productivity based on correlations      between MI and productivity.                                             

In considering Table II, the results in runs 1, 2, 3, 6, 7 and 10 reveal atidentical conditions, except for increasing temperature during sulfiding, that a sulfiding temperature of about 600°-700° C. is about optimum for activation process A in which reoxidation at 593° C. inair was observed. Runs 1 and 2 show that under the conditions employed, sulfiding temperatures ranging from about 260° to about 399°C. are too low thus only minimal benefits in improving melt index capability of catalyst are realized. When the sulfiding temperature reaches about 538° C., run 3 shows that a moderate improvement in catalyst melt index capability is occurring. On the other hand, sulfiding temperatures of about 871° C., based on polymer results, are more favorable than those at 538° C. but less favorable than those at about 650°-700° C.

Runs 4, 5 and 8, 9 demonstrate that activation process B is ineffective in improving melt index capability of catalyst even when sulfiding and reoxidation is employed. These runs employ a combination of the less preferred technique of the invention in that the sulfiding temperature is relatively low (i.e. never reaches the most prefered level of at least 700° C.) and the reoxidation temperature is not lower than the sulfiding temperature. Finally, the polymerization temperature is low. Thebroader molecular weight distribution is due to lower reactor temperature.

It is concluded therefore, that catalyst sulfiding should occur at least about 538° C. more preferably about 600°-700° C. Following this treatment, the catalyst should be heated to about 871° C. in an inert gas as nitrogen, then reoxidized at about 600° C. in an oxygen-containing medium in order to maximize the melt index capability benefits to be expected.

Control run 11 shows a typical result for a cogel catalyst (which represents the best of the prior art catalysts) without sulfiding.

EXAMPLE 3

Portions of the stock catalyst of Example 1 were individually activated in the presence of an organic sulfide compound alone and in the presence of an oxygen-containing organic compound or water. After reoxidation in air, the recovered catalyst was employed in ethylene polymerization as before. The compounds and activation conditions employed and results obtained are presented in Table III. All reoxidations were conducted at 1100° F.unless indicated otherwise.

                                      TABLE III                                    __________________________________________________________________________     Ethylene Polymerization Over Sulfided and Reoxidized Catalysts                 __________________________________________________________________________                           Weight Ratio                                             Run Activation.sup.(1)                                                                    Sulfiding Agent                                                                           Catalyst                                                                               Component 2                                      No. Process                                                                               Type    (g)                                                                               Sulfiding Agent                                                                        Type  (g)                                        __________________________________________________________________________     1   A      methanethiol                                                                           30 0.4:1   none  --                                         2   B      diethyl disulfide                                                                      0.99                                                                              11:1    none  --                                         3   B      diethyl disulfide                                                                      0.99                                                                              11:1    none  --                                         4   B      dimethyl sulfide                                                                       0.85                                                                              13:1    none  --                                         5   B      dimethyl sulfide                                                                       0.42                                                                              26:1    methanol                                                                             0.40                                       6   B      dimethyl sulfide                                                                       0.42                                                                              26:1    acetic acid                                                                          0.52                                       7   B      dimethyl disulfide                                                                     0.20                                                                              54:1    none  --                                         8   B      dimethyl disulfide                                                                     0.50                                                                              22:1    none  --                                         9   B      dimethyl disulfide                                                                     0.99                                                                              11:1    none  --                                         10  B      dimethyl disulfide                                                                     0.50                                                                              22:1    acetic acid                                                                          0.52                                       11  B      dimethyl sulfite                                                                       1.0                                                                               11:1    none  --                                         12  B      sulfur  2   5:1    none  --                                          13.sup.(2)                                                                        B      carbon disulfide                                                                       1.3                                                                                8:1    none  --                                         14  B      carbon disulfide                                                                       1.3                                                                                8:1    none  --                                         15  B      carbon disulfide                                                                       1.3                                                                                8:1    H.sub.2 O                                                                            0.5                                        16  B      carbon disulfide                                                                       0.63                                                                              17:1    methanol                                                                             0.40                                       17  B      carbon disulfide                                                                       0.63                                                                              17:1    acetic acid                                                                          0.52                                       18  C      carbon disulfide                                                                       1.3                                                                                8:1    (CO)                                              19.sup.(3)                                                                        D      carbon disulfide                                                                       1.3                                                                                8:1    (CO)                                              20.sup.(3)                                                                        E      carbon disulfide                                                                       1.3                                                                                8:1    (benzene)                                                                            0.88                                       __________________________________________________________________________     Mole Ratio  Polymerization                                                                         Polymer                                                    Run  Sulfiding Agent                                                                       Run Time                                                                               Adjusted                                                                            HLMI                                                                               Productivity                                      No. Component 2                                                                            (min).sup.(4)                                                                          MI   MI  g/g catalyst                                      __________________________________________________________________________     1   --      48      16   40  5430                                              2   --      38      34   32  4710                                              3   --      85      4.2  43  5370                                              3   --      85      4.2  43  5370                                              4   --      59      9.9  42  5320                                              5   0.5:1   50      24   35  4780                                              6   0.8:1   45      22   30  4770                                              7   --      34      9.6  41  4620                                              8   --      52      12   47  5000                                              9   --      67      5.6  45  5060                                              10  0.6:1   53      19   47  5050                                              11  --      dead    --   --  --                                                12  --      57      6.7  43  5100                                               13.sup.(2)                                                                        --      59      18   44  5460                                              14  --      50      9.1  37  5150                                              15  0.6:1   28      21   36  5310                                              16  0.7:1   52      18   37  5180                                              17  0.9:1   40      28   31  4940                                              18          35      20   36  4650                                               19.sup.(3) 63      12   42  4890                                               20.sup.(3)                                                                        1.5:1   51      7.9  43  5000                                              __________________________________________________________________________      .sup.(1) Activation Process                                                   A. Air to 1200° F.; 5 min. N.sub.2 flush; CH.sub.3 SH gas (42 1/hr       for 20 min) at 1200° F.; switch to N.sub.2, raise temperature to        1600° F. and hold 2 hours; lower temperature in N.sub.2 to              1000° F.; switch to air and hold 2 hours at 1100° F.; cool       and recover catalyst.                                                         B. Air to 1600° F.; 1 min. N.sub.2 flush; inject additives into          N.sub.2 stream; hold in N.sub.2 for 2 hours; lower temperature in N.sub.2      to 1100° F.; switch to air and hold 1 hour at 1100° F.; coo     and recover catalyst.                                                          C. Air to 1600° F.; 1 min. N.sub.2 flush; inject 1 ml CS.sub.2 into      N.sub.2 stream; hold in N.sub.2 about 10 min; switch to CO and hold in CO      for 2 hours at 1600° F.; flush with N.sub.2, lower temperature to       1200° F.; switch to air and hold 2 hours, cool and recover              catalyst.                                                                     D. Same procedure as C except treating order in CS.sub.2 and CO is              reversed.                                                                     E. Air to 1600° F.; 1 min. N.sub.2 flush; 1 ml benzene injected in       N.sub.2 stream; hold in N.sub.2 about 10 min; lower temperature in N.sub.     to 1200  F.; switch to air and hold for 2 hours at 1200° F.; cool        and recover catalyst.                                                          .sup.(2) Run 10 of Table II repeated here.                                     .sup.(3) Note that catalyst is treated with component 2 before component       1.                                                                             .sup.(4) All runs at 225° F. (107° C.).                    

Inspection of Table III shows in runs 1, 2, 5, 6 and 8 that active catalysts result when one of the compounds listed is used in sulfiding thecatalyst. However, erratic results have been noted with respect to large deviations in expected polymer melt index produced with such catalysts. Run 2 polymer MI is 34 whereas run 3 is 4.2, both polymers being produced from catalyst prepared in a similar way but in separate runs. This effect is illustrated with another sulfiding agent in runs 13 and 14. The addition of an oxygen containing organic compound or even water during sulfiding has eliminated the problem, resulting in generally reproducible results from run to run. This is illustrated, for example, in runs 15, 16 and 17 which are comparable with run 13. Runs 18-20 illustrate a two step reducing stage for catalyst activation followed by reoxidation. Melt indexcapability of the catalyst is improved by such treatment although no pronounced advantage is apparent over the procedure employed with a singleorganic sulfur compound. In comparing runs 18 and 19 in a two step reducingstage employing an organic sulfur compound and CO, the best results are obtained (run 18) when the catalyst is contacted with the organic compoundprior to contact with CO.

EXAMPLE 4

Based on the results obtained in Example 3, another series of sulfided and reoxidized catalyst samples was prepared. Since oxygen containing organic compounds generally decompose into CO, H₂ and C at about 1600°F., this suggests that sulfiding is best carried out in the presence of CO.Carbonyl sulfide (COS) is a convenient source of both sulfur and CO when itdecomposes at about 1600° F. Catalyst was prepared by sulfiding samples of the stock catalyst of Example 1 with a mixture of 10 mole percent COS in nitrogen, for various times at 1600° F. and reoxidized in air at 1100° F. EAch recovered catalyst was used to polymerize ethylene as before. The activating conditions employed and results obtained are presented in Table IV.

                                      TABLE IV                                     __________________________________________________________________________     Ethylene Polymerization Over Catalysts Sulfided With COS                                           Polym.                                                                               Polymer                                              Run                                                                               COS Treatment                                                                           Weight Ratio                                                                           Run Time                                                                             Adjusted                                                                            HLMI                                                                               Productivity                                No.                                                                               min.                                                                              g (nominal)                                                                          Catalyst/COS                                                                           min.  MI   MI  g/g cat.                                    __________________________________________________________________________     1  15 2.8   3.9:1   52    13   45  5420                                        2  30 5.6   1.9:1   40    34   34  5240                                        3  60 11      1:1   30    45   33  5350                                        4  120                                                                               22    0.5:1   54    36   35  5230                                        __________________________________________________________________________

All runs at 225° F. (107° C.) reactor temperature.

Activating process consisted of heating catalyst in air to 1600° F.;1 min. N₂ flush; inject sufficient COS into N₂ stream to obtain amixture containing 10 mole % COS and contact catalyst for the specified time; continue heating in N₂ only for 2 hours; reduce temperature to 1100° F. in N₂ ; switch to air and hold for 2 hours at 1100° F.; cool and recover catalyst.

The melt index results in Table IV clearly demonstrate the efficacy of an activation treatment comprising sulfiding the catalyst with carbonyl sulfide and reoxidizing it. Under the conditions employed, run 3 shows theactivation process yielded a catalyst that in particle form ethylene polymerization produced an ethylene homopolymer exhibiting a melt index of

In summary, the activation treatment disclosed in this invention yields catalysts which in contact with ethylene in a particle form polymerizationprocess at 225° F. (107° C.) are capable of routinely producing polyethylene which have melt index values in the 30 to about 50 range. The polymers are shown by gel permeation chromatographs to have rather narrow molecular weight distributions, i.e. 3.9 for a 20 melt indexpolymer (this is the ratio of weight average molecular weight to number average molecular weight, i.e. M_(w) /M_(n) and can be found by GPC). This value approaches the values obtained for similar melt index polymers made in a solution process. The high melt index narrow molecular weight distribution polymers made with the invention catalysts appear to be quitesuitable for injection molding, for example.

The sulfiding procedure is satisfactorily carried out in quartz or ceramic activators. However, since metal embrittlement may result at the high temperatures employed in the presence of the organic sulfur compounds caution is indicated when activators constructed of certain metals or metal alloys such as Inconel are employed.

EXAMPLE 5

The purpose of this example is to show the relative values for melt index (with other variables held constant) for (1) the best prior art catalyst, a titanium cogel with ordinary air oxidation, (2) CO treatment which is animprovement over the basic catalyst and is the subject of a separate invention, and (3) the sulfiding of this invention. The stock catalyst, ineach instance, was a nominal 2 percent titanium cogel with a nominal 1 percent chromium content as in the prior Examples. The data are set out inTable V.

                                      TABLE V                                      __________________________________________________________________________     CO       COS         Air   Polymerization                                      Treatment                                                                               Treatment                                                                            Reoxidation                                                                          Activation                                                                           Run Run Polymer                                     Run                                                                               Temp. Temp. Temp. Temp. Time                                                                               Temp.                                                                              Adjusted                                                                            HLMI                                                                               Productivity                       No.                                                                               °C.                                                                           °C.                                                                           °C.                                                                           °C.                                                                           min.                                                                               °C.                                                                         MI   MI  g/g Catalyst                       __________________________________________________________________________     1  --    --    --    871   75  107 2.8  46  5620                               2  871   --    650   --    62  107 9.1  36  4850                               3  --    871   593   --    30  107 45   33  5350                               __________________________________________________________________________

Each of runs 1, 2 and 3 are run under essentially optimum conditions for that system. As can be seen, invention run 3 gave a melt index of 45 whichis almost five times that of control run 2 and sixteen times control run 1.To further put this in perspective, control run 1 represents the best of the prior art chromium oxide systems, MI values of less than 1 being obtained with ordinary chromium on silica catalysts under these conditions.

While this invention has been described in detail for the purpose of illustration, it is not to be construed as limited thereby but is intendedto cover all changes and modifications within the spirit and scope thereof. 

We claim:
 1. A polymerization process comprising contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule under polymerization conditions with an oxidized chromium-containing catalyst prepared by a process comprising a first step wherein a composition comprising a chromium component on a silica-containing base is contacted with an organic sulfur-containing ambient at a temperature of at least 370° C., chromium of said chromium component being at least partially in the hexavalent state and a subsequent second step wherein the thus treated composition is contacted with an oxygen-containing oxidizing ambient at a temperature within the range of 350°-900° C. to produce said oxidized chromium-containing catalyst
 2. A method according to claim 1 wherein said olefin is selected from ethylene, propylene, and 1-butene.
 3. A method according to claim 1 wherein said olefin is predominantly ethylene.
 4. A method according to claim 1 wherein said polymerization is carried out at a temperature within the range of 66°-110° C.
 5. A method according to claim 1 wherein said composition is heated in the presence of oxygen prior to said contact with said sulfur-containing ambient.
 6. A method according to claim 5 wherein after said heating in the presence of oxygen, a nitrogen ambient is introduced to flush out the air prior to said introduction of said sulfur-containing ambient.
 7. A method according to claim 6 wherein said nitrogen flush is carried out for less than 30 minutes.
 8. A method according to claim 5 wherein said contact with said sulfur-containing ambient is at a temperature within the range of 600°-900° C. and said second step is carried out at a temperature within the range of 450°-700° C., which temperature is also at least 50° C. lower than said temperature for contact with said sulfur-containing ambient.
 9. A method according to claim 8 wherein said contact with said sulfur-containing ambient is for a time within the range of 10 minutes to 3 hours and said second step is carried out for a time within the range of 1 to 4 hours.
 10. A method according to claim 1 wherein said composition is heated in air to a temperature within the range of 250°-1000° C. over a time period of at least 5 minutes prior to said contact with said sulfur-containing ambient.
 11. A method according to claim 1 wherein said sulfur-containing ambient comprises a sulfur-containing material and an oxygen-containing compound.
 12. A method according to claim 11 wherein said oxygen-containing compound is selected from acetic acid, methanol or water vapor and said sulfur-containing material is selected from dimethyl sulfide, methylmercaptan, diethyl sulfide, and carbon disulfide.
 13. A method according to claim 1 wherein said sulfur-containing ambient comprises carbon disulfide.
 14. A method according to claim 1 wherein said sulfur-containing ambient comprises carbonyl sulfide.
 15. A method according to claim 1 wherein said silica-containing base is a cogel formed by adding a titanium compound to a mineral acid, introducing an alkali metal silicate into the acid containing said titanium compound to form a hydrogel, aging the hydrogel for a time of greater than one hour, washing the thus aged hydrogel to produce a substantially alkali metal free hydrogel, forming a mixture comprising the thus washed hydrogel and a normally liquid oxygen-containing water soluble organic compound, and separating said organic compound and water from said mixture to form a xerogel, and wherein said chromium is imparted by impregnation of said hydrogel with an aqueous chromium acetate solution, said catalyst consisting essentially of said chromium and silica components.
 16. A method according to claim 15 wherein said olefin is predominantly ethylene.
 17. A method according to claim 1 wherein said oxidized chromium-containing catalyst contains less than 0.4 weight percent sulfur.
 18. A method according to claim 1 wherein said contacting with said sulfur-containing ambient and said subsequent contact with an oxygen-containing ambient is carried out in a continuous activator.
 19. A process according to claim 1 wherein said silica-containing base is a silica-titania cogel containing about 2 weight percent titania based on the weight of said cogel, said chromium component being present in an amount sufficient to give about 0.5 to 1 weight percent chromium based on the weight of said base, said sulfur-containing ambient is carbonyl sulfide and wherein said contacting with said carbonyl sulfide is carried out at a temperature within the range of 600°-900° C. for a time within the range of 10 minutes to 3 hours and wherein said oxidizing ambient is air and said contact with said air is carried out at a temperature within the range of 450°-700° C. for a time within the range of 1 to 4 hours and wherein said chromium-containing catalyst is heated in air at a temperature within the range of 700°-925° C. prior to said contact with said carbonyl sulfide.
 20. A polymerization process comprising contacting at least one mono-1-olefin having 2 to 8 carbon atoms per molecule under polymerization conditions with a catalyst consisting essentially of a chromium component and a silica-containing base said catalyst being prepared by a process comprising a first step wherein a composition comprising a chromium component on a silica-containing base is contacted with an organic sulfur-containing ambient at a temperature of at least 370° C., chromium of said chromium component being at least partially in the hexavalent state and a subsequent second step wherein the thus treated composition is contacted with an oxygen-containing oxidizing ambient at a temperature within the range of 350°-900° C.
 21. A method according to claim 20 wherein said composition is heated in the presence of oxygen prior to said contact with said sulfur-containing ambient.
 22. A method according to claim 21 wherein after said heating in the presence of oxygen, a nitrogen ambient is introduced to flush out the oxygen prior to said introduction of said sulfur-containing ambient.
 23. A method according to claim 22 wherein said nitrogen flush is carried out for less than 30 minutes.
 24. A method according to claim 23 wherein said contact with said sulfur-containing ambient is at a temperature within the range of 600°-900° C. and said second step is carried out at a temperature within the range of 450°-700° C., which temperature is also at least 50° C. lower than said temperature for contact with said sulfur-containing ambient.
 25. A method according to claim 24 wherein said contact with said sulfur-containing ambient is for a time within the range of 10 minutes to 3 hours and said second step is carried out for a time within the range of 1 to 4 hours.
 26. A method according to claim 20 wherein said composition is heated in air to a temperature within the range of 250°-1000° C. over a time period of at least 5 minutes prior to said contact with said sulfur-containing ambient.
 27. A method according to claim 20 wherein said sulfur-containing ambient comprises a sulfur-containing material and an oxygen-containing compound.
 28. A method according to claim 27 wherein said oxygen-containing compound is selected from acetic acid, methanol or water vapor and said sulfur-containing material is selected from dimethyl sulfide, methylmercaptan, diethyl sulfide, and carbon disulfide.
 29. A method according to claim 20 wherein said sulfur-containing ambient comprises carbon disulfide.
 30. A method according to claim 20 wherein said sulfur-containing ambient comprises carbonyl sulfide.
 31. A method according to claim 20 wherein said silica-containing base is a cogel formed by adding a titanium compound to a mineral acid, introducing an alkali metal silicate into the acid containing said titanium compound to form a hydrogel, aging the hydrogel for a time of greater than one hour, washing the thus aged hydrogel to produce a substantially alkali metal free hydrogel, forming a mixture comprising the thus washed hydrogel and a normally liquid oxygen-containing water soluble organic compound, and separating said organic compound and water from said mixture to form a xerogel, and wherein said chromium is imparted by impregnation of said hydrogel with an aqueous chromium acetate solution.
 32. A method according to claim 20 wherein said catalyst contains less than 0.4 weight percent sulfur.
 33. A method according to claim 20 wherein said contacting with said sulfur-containing ambient and said subsequent contact with an oxygen-containing ambient is carried out in a continuous activator.
 34. A process according to claim 20 wherein said silica-containing base is a silica-titania cogel containing about 2 weight percent titania based on the weight of said cogel, said chromium compound being present in an amount sufficient to give about 0.5 to 1 weight percent chromium based on the weight of said base, said sulfur-containing ambient is carbonyl sulfide and wherein said contacting with said carbonyl sulfide is carried out at a temperature within the range of 600°-900° C. for a time within the range of 10 minutes to 3 hours and wherein said oxidizing ambient is air and said contact with said air is carried out at a temperature within the range of 450°-700° C. for a time within the range of 1 to 4 hours and wherein said composition is heated in air at a temperature within the range of 700°-925° C. prior to said contact with said carbonyl sulfide.
 35. A method according to claim 20 wherein said olefin is selected from ethylene, propylene and 1-butene.
 36. A method according to claim 20 wherein said olefin is predominantly ethylene.
 37. A method according to claim 20 wherein said polymerization is carried out at a temperature within the range of 66° to 110° C. 